PDF《制氢站冷却器换热管泄漏原因分析》

第47卷第4期2010年8月 化工设备与管道 PROCESS EQUIPMENT&PlPlN(;

VoL47 No.

4 Au昏2010 ・材料与防腐・ 制氢站冷却器换热管泄漏原因分析 毛华群 (宝钢工业检测公司,上海201900) 摘要:针对某公司制氢站一台冷却器换热管多处腐蚀穿孔泄漏现象,通过对其换热管化学成分分析、管子表面腐 蚀产物形貌分析、腐蚀产物成分能谱分析、管子金相组织分析和水质分析,结果发现换热管失效原因是与循环冷却 水质和流速缓慢有关. 关键词:换热管;

失效;

点腐蚀 中图分类号:1'Q 050.9+l 文献标识码:A 文章编号:1009_328l(2010)04JD055∞3 Causes Analysis of Leakage occurred in Heat TransfIer Tube in Cooler Used in Hydrogen Generation Station MAO Hua-qun (觑d淞#砌z如Pec渤n co.,占∞&纠,s妇,神口i 2DJ9DD,饥im) Abstract: With respectto the leakage due to co肿sion occuⅡ℃d in 8everal locations in the heat响nsfer tubes in a cooIer used in a hydrogen generation station,the chemicaI and metallu蟛cal comPosition of the tubes,the su"hce fb咖and the composition energy spec. tmm o"he co兀Dsion products and the water毋.稍ng in the tubes were analyzed.7rhe result showed that the failure"the tubes was due to the composition of the cycling water and the low velocity 0f the water. Keywords: heat transfer tube;

failure;

dot co兀.0sion 某公司制氖站焦炉煤气冷却器使用20个月就 出现4根换热管子局部腐蚀穿孔现象.该换热器自 2004年7月制造,2005年5月功能考核结束投用, 而且非满负荷运行.换热器结构为卧式固定管板式 换热器型式,管内走焦炉原料煤气,管外走冷冻循环 水.冷却器外观主要技术参数见表l. 表1冷却器主要技术参数 .. 参数 壳程 管程

1 宏观形貌观察 失效换热管外表面覆盖~层厚薄不均匀的沉积 物,靠近折流板的部位分布着一些大小不一的蚀坑, 呈溃疡状,出现腐蚀减薄现象,腐蚀严重的部位已经 穿透,蚀孔径约5 mm.从抽出的多根管子来看,在 靠近一些折流板附近都有这种腐蚀情况,但折流板 的其他部位无此现象,内表面也未发现腐蚀,说明腐 蚀是从外表面开始向内表面发展,腐蚀有可能与折 流板位置有关,也可能与管外的循环水质有关. 2化学成分分析 对取样换热管子材料的化学成分进行分析,判 断材料是否有异常,表2为管子化学成分测试结果, 符合20钢标准. 表2换热管化学成分 % 项日 C Si Mn P S 实测值 O.19 O.20 O.48 O.009